Page 19 - index

GT 1000 GT 1000 FLEX

SILVER-PLATED COPPER FILLED SILVER-PLATED COPPER
SILICONE CONDUCTIVE SILICONE

• Low density (2.67g.cm )
3
• Good EMP resistance • Low compression force
• Low degassing rate • Very low RDC (<10%)
• Both electrically and thermally conductive • Highly conductive
• Excellent stability over time • Excellent attenuation performance
• Very high stability over time

Thanks to its space qualification according to the ESA-ECSS-Q-ST-70-02C TML RML (<1%)
and CVCM (<0.1%) standard, the GT1000 FLEX is suitable for aerospace application.
Thanks to its space qualification according to the ESA-ECSS-Q-ST-70-02C TML RML (<1%) and CVCM (<0.1%)
standard, the GT 1000 is suitable for aerospace applications.
Compression measurement GT1000 FLEX
Properties Standards - Test GT 1000 Flex
Elastomer Silicone
Silver-plated
Conductive filler
copper
Standards - Specification Volume resistivity (Ω.cm) < 0.005
Properties GT 1000
Tests MIL G 83528
Hardness (Shore A) ASTM D 2240 40 Compressive stress (MPa)
Type MIL G 83528 Type K
Density (g/cm ) ASTM D 792 Method A 2.67
3
Elastomer Silicone
Break resistance (Mpa) ASTM D 412 Method A C 0.81
Silver-plated
Conductive filler
copper Elongation at break (%) ASTM D 412 Method A C 250
Volume resistivity (Ω.cm) MIL G 83528 < 0.005 0.005
Tear strength (N/mm) ASTM D 624 C 3.89
Hardness (shore A) ASTM D 2240 82 85 ±7 Deformation (%)
ASTM D 792 Residual deformation after
3
Density (g/cm ) Method A 3.40 3.50 ± 13% compression 70 hours at 100°C ASTM D 395 Method B 6.3 %
2.76
Break resistance (Mpa) ASTM D 412 2.80 Minimum Working temperature -55°C to+125°C Attenuation curve GT1000 FLEX
Method A C
TML (%) ECSS-ST-70-02C 0.37
Elongation at break (%) ASTM D 412 250 100-300
Method A C available formats RML (%) ECSS-ST-70-02C 0.37
Tear resistance 13.44 7.0 CVCM (%) ECSS-ST-70-02C 0.07
(N/mm) ASTM D 624 C Minimum Molded Color Grey / Beige
Residual deformation after 35 Customized cutting SE (dB)
compression 70 hours at 100°C ASTM D 395 17.50 Maximum
(%) Method B Extruded
Continuous operating -55°C to +125°C -55°C° Adhered by vulcanization available formats
temperature to+125°C
Color Grey / Beige Sheet Molded
Frequency (MHz)
Adhesive Customized cutting
Adhered by vulcanization
Sheet
Extruded

18
375 Avenue Morane Saulnier 78530 - Buc, France www.getelec.com 18 www.getelec.com 19
Tel : +331 39 20 42 42 | info@getelec.com