Page 37 - index

GT 5007 GT 5200

SILVER-PLATED ALUMINUM FILLED SILVER-PLATED ALUMINUM FILLED
CONDUCTIVE FLUOROSILICONE • Low density CONDUCTIVE EPDM

• Excellent high-frequency performance • Gas permeable
• Good abrasion resistance
• Compatible with most alloy • Good high temperature resistance
• Very stable at high temperature (190°C peak)
(200°C peak) • Excellent mechanical performance
• Resistance to solvents, oils, • Resistant to methyl, ethyl, ketone type
hydrocarbons or hydraulic fluids aggressive solvents

Properties Standards - GT 5007 Specification Properties Standards - Tests GT 5200
Tests MIL G 83528
Type MIL G 83528 D - Type MIL G 83528 -

Elastomer Fluorosilicone - Elastomer EPDM
Conductive filler Silver-Plated - Conductive filler Silver-plated
aluminum
aluminum
0.012
Volume resistivity (Ω.cm) MIL G 83528 < 0.0029 Maximum Volume resistivity (Ω.cm) MIL G 83528 < 0.015
Hardness (shore A) ASTM D 2240 71 70 ± 7 Hardness (shore A) ASTM D 2240 70
ASTM D 792
3
ASTM D 792 Density (g/cm ) Method A 2.00
Density (g/cm ) 2 2 ± 13%
3
Method A Break resistance (Mpa) ASTM D 412 1.70
1.24
Break resistance (Mpa) ASTM D 412 1.85 Minimum Method A C
Method A C
ASTM D 412
470
Method A C
Elongation at break (%) ASTM D 412 260 60-260 Elongation at break (%) ASTM D 624 C 12.00
Method A C
Tear resistance (N/mm)
6.13
Tear resistance (N/mm) ASTM D 624 C 7.36 Minimum Residual deformation after
compression 70 hours at ASTM D 395 40
Residual deformation after 30 100°C (%) Method B
compression 70 hours at 100°C ASTM D 395 21 Maximum Continuous operating
(%) Method B temperature -45°C to +160°C
Continuous operating -55°C to+160°C -55°C to available formats Color Grey available formats
temperature +160°C
Color Blue / light grey - Molded
Molded
Customized cutting Customized cutting
Extruded Extruded
Adhered by vulcanization Adhered by vulcanization
Sheet Sheet

Adhesive Adhesive

36