GT 3000 GT 3007

SILVER-PLATED NICKEL FILLED SILVER-PLATED NICKEL FILLED
CONDUCTIVE SILICONE CONDUCTIVE FLUOROSILICONE

• Very stable temperature range
• Very stable temperature range • Irregular particle shape for better particle
• Irregular particle shape for better contact
particle contact • Good corrosion resistance on aluminum
• Good corrosion resistance on support (168 hours test in salt spray)
aluminum support (168 hours test
in salt spray)

Properties Standards - GT 3000 Specification
Tests MIL G 83528 Standards -
Type MIL G 83528 L - Properties Tests GT 3007
Type MIL G 83528 -
Elastomer Silicone -
Silver- Elastomer Fluorosilicone
Conductive filler plated -
Nickel Conductive filler Silver-plated
Nickel
Volume resistivity (Ω.cm) MIL G 83528 < 0.005 0.005 Volume resistivity (Ω.cm) MIL G 83528 < 0.006
Hardness (shore A) ASTM D 2240 75 75 ± 7 Hardness (shore A) ASTM D 2240 60
Density (g/cm ) ASTM D 792 3.70 4.00 ±13% Density (g/cm ) ASTM D 792 3.50
3
Method A
3
Method A
Break resistance (Mpa) ASTM D 412 3.00 1.38 ASTM D 412
Method A C Minimum Break resistance (Mpa) Method A C 2.40
Elongation at break (%) ASTM D 412 290 100-300 ASTM D 412
Method A C Elongation at break (%) Method A C 250
Tear resistance 5.25 Tear resistance
(N/mm) ASTM D 624 C 9.50 Minimum (N/mm) ASTM D 624 C 7.50
Residual deformation after
compression 70 hours at 100°C ASTM D 395 < 32 32 maximum Residual deformation after ASTM D 395 < 35
Method B
(%) compression 70 hours at 100°C (%) Method B available formats
Continuous operating -55°C to -55°C to available formats -55°C to
temperature +125°C +125°C Continuous operating temperature +125°C Molded
Color Grey - Molded Color Grey / Beige Customized cutting
Customized cutting
Extruded
Extruded
Adhered by vulcanization
Adhered by vulcanization
Sheet
Sheet
Adhesive
Adhesive