Innovative solution, our GT5068 was developed by combining a conductive silicone filled with silver-plated aluminum (GT5000) with a doped EPDM silicone 65 Shore. This mixture is intented to meet the constraints of a corrosive environment by seprataing the shielding function and the sealing function to respond to specific applications.
| Properties | Standards - Tests | GT5000 | EPDM-Si |
|---|---|---|---|
| Elastomer | Silicone | EPDM - Si | |
| Conductive filler | Silver-plated aluminum | ||
| Volume resistivity (Ω.cm) | MIL G 83528 | < 0.0054 | |
| Hardness (Shore A) | ASTM D 2240 | 65 | 65 |
| Density (g/cm3) | ASTM D 792 Method A | 1.90 | 1.45 |
| Break resistance (Mpa) | ASTM D 412 Method AC | 1.89 | 6.4 |
| Elongation at break (%) | ASTM D 412 Method AC | 286 | 486 |
| Tear strength (N/mm) | ASTM D 624 C | 8.43 | 25.4 |
| Residual deformation after compression 70 hours at 100°C (%) | ASTM D 395 Methode B | 17.30 | |
| Workting temperature (°C) | -55°C to +160°C |
Our corrosion-resistant bi-material EMC solutions are available as extruded profiles, moulded seals, die-cut or adhered to your substrate. This process is also applicable to equipment housing covers by direct vulcanisation in our workshops.
Our know-how and our support policy also includes taking into account your constraints and tolerances, which is why all of our solutions can be made to measure according to your specific plans and manufacturing processes within a short timeframe.